Three-dimensional cartilage-carrier-constructs were produced according to a standard protocol from chondrocytes of an adult mini-pig. Experiments with different oxygen concentrations (21, 10 and 5%, v/v O(2)) were performed and the constructs were compared qualitatively and quantitatively. The appearance of the cartilage obtained under reduced oxygen tension seemed to be closer to native cartilage with respect to shape of the cells, distribution of the cells within the matrix, smoothness of the surface, etc. The thickness of the cartilage formed by free swelling was always in the same range as for native cartilage (approximately 1mm). Qualitatively the most stable attachment of the cartilage on top of the carrier was found for 10% O(2) (v/v). Especially at 5% O(2) (v/v) the attachment between cartilage and carrier was not sufficient. The constructs generated at lower oxygen tensions had a significantly higher amount of glycosaminoglycan per DNA, but still significantly less when compared to native cartilage. Furthermore, the cultivated cartilage contained a large amount of collagen type II. The experiments proved the applied concept for generation of cartilage-carrier-constructs and the usefulness of cultivation under reduced oxygen tension.