Effect of luting agents and reconstruction techniques on the fracture resistance of pre-fabricated post systems.
Standard
Effect of luting agents and reconstruction techniques on the fracture resistance of pre-fabricated post systems. / Toksavul, S; Toman, M; Uyulgan, B; Schmage, Petra; Nergiz, Ibrahim.
In: J ORAL REHABIL, Vol. 32, No. 6, 6, 2005, p. 433-440.Research output: SCORING: Contribution to journal › SCORING: Journal article › Research › peer-review
Harvard
APA
Vancouver
Bibtex
}
RIS
TY - JOUR
T1 - Effect of luting agents and reconstruction techniques on the fracture resistance of pre-fabricated post systems.
AU - Toksavul, S
AU - Toman, M
AU - Uyulgan, B
AU - Schmage, Petra
AU - Nergiz, Ibrahim
PY - 2005
Y1 - 2005
N2 - Fracture resistance and fracture modes of endodontically treated maxillary central incisors restored with different post-and-core systems covered with all-ceramic copings were evaluated. Ten samples were prepared for each group. Groups 1, 2 and 3 consisted of tooth-coloured post-and-core, zirconia post (Cosmopost) with a composite core (Tetric Ceram), zirconia post (Cosmopost) with a custom made ceramic core (Cosmo Ingot), glass fibre-reinforced post (FRC Postec) with a composite core (Tetric Ceram), respectively. Group 4 consisted of a titanium post (ERpost) with a composite core (Tetric Ceram). The control group (group 5) consisted of root-filled incisors without posts. Tooth-coloured posts were cemented in the roots using Variolink-2, while titanium posts were cemented in the roots using Harvard cement. The all-ceramic copings were cemented using Variolink-2. Static load was applied to 2 mm below the incisal edge on the palatinal surface of each sample until they were fractured. Fracture data were obtained and statistically analysed with One-way anova and a Tukey's test. The results of the means and standard deviations of the fracture resistance during static loading were: 497.5 +/- 61.94 (1), 474.61 +/- 96.84 (2), 494.61 +/- 104.67 (3), 581.34 +/- 105.36 (4), 420.42 +/- 127.48 (5). There were statistically significant differences between groups 4 and 5. Glass fibre-reinforced posts and composite cores (group 3) showed the most catastrophic failure. Consequently, zirconia ceramic posts can be used in clinical practice.
AB - Fracture resistance and fracture modes of endodontically treated maxillary central incisors restored with different post-and-core systems covered with all-ceramic copings were evaluated. Ten samples were prepared for each group. Groups 1, 2 and 3 consisted of tooth-coloured post-and-core, zirconia post (Cosmopost) with a composite core (Tetric Ceram), zirconia post (Cosmopost) with a custom made ceramic core (Cosmo Ingot), glass fibre-reinforced post (FRC Postec) with a composite core (Tetric Ceram), respectively. Group 4 consisted of a titanium post (ERpost) with a composite core (Tetric Ceram). The control group (group 5) consisted of root-filled incisors without posts. Tooth-coloured posts were cemented in the roots using Variolink-2, while titanium posts were cemented in the roots using Harvard cement. The all-ceramic copings were cemented using Variolink-2. Static load was applied to 2 mm below the incisal edge on the palatinal surface of each sample until they were fractured. Fracture data were obtained and statistically analysed with One-way anova and a Tukey's test. The results of the means and standard deviations of the fracture resistance during static loading were: 497.5 +/- 61.94 (1), 474.61 +/- 96.84 (2), 494.61 +/- 104.67 (3), 581.34 +/- 105.36 (4), 420.42 +/- 127.48 (5). There were statistically significant differences between groups 4 and 5. Glass fibre-reinforced posts and composite cores (group 3) showed the most catastrophic failure. Consequently, zirconia ceramic posts can be used in clinical practice.